Box 71092Springfield, OR 97475. Since you have muriatic acid, its really easy to make ferric chloride. It is the ideal acid etch alternative. For etching, you'll find a confusing array of products, including standard muriatic acid as well as products such as Klean-Strip Green Muriatic Acid ($7.84 per gallon at Home Depot) and. Edit* I just realized folks already gave this answer. If the reaction is proceeding too slowly for your liking you can heat up the mixture. You can do this by first mixing a small solution in your watering can starting at a 5:1 ratio. Etching acids can range from powerful hydrochloric or sulfuric acid to much weaker acids even household vinegar, citrus fruit, or mustard can be used effectively. Acid Etch: Disassemble your knife, and thoroughly clean and dry the part you're going to etch (blade, handle, or clip). It does not contain phosphoric, hydrochloric or muriatic acid, yet works better, safer and faster. NOT ALL DAMASCUS ARE MADE LIVING Damascus is made of many metallic combinations to form one piece. Or is there more of a process? Erik takes the lead with this video because it's his specialty, he shows how to clean the blades, prepare them for etching, etch them, neutralize them, polish after etching, and a lot of other little tricks in between. Like is itmore effective on a piece ground to 120, than one polished to 1000? Ive never gotten a uniform etch on an HI khuk, even when soaking the blade completetly in the solution. While high in carbon steel, the blade can easily rust if not cared for. Shop Talk - BladeSmith Questions and Answers. Professional Strength 31.45% HCL (Muriatic Acid), excellent for pH reduction in swimming pools or to clean and etch masonry surfaces, excellent for pH reduction in all commercial and residential pools.Find the ACID MURIATIC GAL at Ace. You can order it off of Amazon, believe it or not. Stainless Steel and Damascus, Kitchen Knives and Other Specialty Knives, Knife Making Parts : Finger Guards and Butt Caps, Metal Buffing, Grinding and Sanding Tools & Supplies, Knife Sheaths, Cases, Edge Guards & Displays, Hock Handplanes, Draw Knives & Spoke Shaves, Special Order & Construction Grade Products. After 10 minutes take it out and give it a quick dip in the bucket of water. Now we're using muriatic acid and loving it. Learn More, click here. . Brush or spray the acid solution on the concrete, wait eight to 10 minutes, then neutralize the acid by spraying. There are significant risks to health and body including maiming and even death. With ferric acid, keep grit between 400 and 600. The HCL (hydrochloric acid) is commonly used in a diluted form called Muriatic Acid for PH balancing in pools. wow sounds like fun. It is commonly used to etch steel and stainless steel parts, but it is also capable of etching copper. Is it just lots of jelly rolls mushed together? Muriatic acid is "hydrochloric acid" (HCl) in a less pure and diluted strength for non-technical applications like cleaning bricks. There are five distinctive patterns from which to choose. Fill a plastic garden watering can halfway with the mixture. In both uric acid and ferric chloride, the temperature should be between 70 and 100 degrees Fahrenheit, about room temperature. Possible acids include muriatic (hydrochloric) acid (HCL), nitric acid (HNO3), or sulfuric acid (H2SO4). Possible acids include muriatic (hydrochloric) acid (HCL), nitric acid (HNO3), or . Can you etch Damascus steel with muriatic acid? i can't wait to mess with it. The iron will start reacting with the acid to produce hydrogen gas and ferrous chloride. It needs to be heated on a hot plate or in a crock pot first. Mix water and acid in 3 or 4:1 ratio. I know at least one ABS Mastersmith that used muriatic acid to etch then blue their bladeshe doesn't much care for Floric Chlorideit isn't deep enough. Thank you Kevin. So I'm lightin' out for the territory, ahead of the scared and the weak and the mean spirited, because Aunt Sally is fixin to adopt me and civilize me, and I can't stand it. You can make a reasonable facsimile of ferric by dissolving steel wool in muriatic acid. Make Ferric Chloride (for etching printed circuit boards). Never use tap water, spring water, or filtered water - all will cause problems etc. [_wpnonce] => You can also use Windex with this step, but do not try to break your piece. What is the Best 2x72 Grinder if you had the money? and I did neutralize with baking soda bath as directed. Do not change before creativity! Clorox wipes and Windex work well for cleaning. Begin the etching process. How do I heat-treat my stainless Damascus after purchase? Dilution should best be done with distilled water to keep it uncontaminated with water minerals. Bought some muriatic acid and hydrogen peroxide, did a mix of 1 muriatic to 2 hydrogen p. Works great, happy with it, now what do i do with it? If you etch before heat treating you'll just erase it in the cleanup sanding. Put on the goggles and vinyl gloves before mixing the chemicals. KMT 106 - Etching Damasteel knife blades with muriatic acid JohnGrimsmo 76.1K subscribers Subscribe 126K views 7 years ago Damasteel is a powdered metallurgy stainless damascus steel. Damascus steel is a famed type of steel recognizable by the watery or wavy light and dark pattern of the metal. This product is a very strong acid that will clean dried cement products off stones, bricks, and other masonry surfaces. One of the reasons it is so popular is because of its versatility. Also the finish can basically be removed with a dry cloth. But in Vegas Forge, they give that and more. FORGE, Jan 1, 2014 #4 Icho- Staff Member Likes Received: 154 Trophy Points: 63 Thanks Forge. Wash thoroughly your piece of liquor and view it with pure oils. This steel had been produced for 11 centuries, and in just about a generation, the means of its manufacture was entirely lost. 2 Remove any burrs on the edges of the steel. It may not display this or other websites correctly. The keys are "pretty dilute" and "multiple, short immersions". Our first Etching Damasteel video:https://www.youtube.com/watch?v=inzrn7kL-2UHere is more information about Damasteel and where to order it from. Furthermore if forged in the correct manner you can make swords from it that depicts a pattern often likened to watered silk. What products are often used? Does etching have to be done before temper, or can you etch first and have the pattern survive the process? We use a laser engraver to engrave on the Damascus steel. The generally accepted shelf life of ferric chloride solution is approximately six months. Of course, it is possible for any smith to have an improper batch, but any frequency of Damascu, Damascus1 creates the best products in America made of Damascus steel. Dampen the surface to be etched with clean water. Putting acid on your travertine will cause it to initially bubble and fizz (CO2 escaping in the reaction). Buy NANFANG BROTHERS Damascus Kitchen Knife Set, 14 Pieces Japanese Knife Set Kitchen Knife Set with Block Wooden, 67 Layers VG10 Damascus Steel Chef Knife Set with Sharpener, Sharp Blades at Amazon UK. Congratulations on your progress. Michael, my advise would be to dilute it down subtantially with distilled water. I did a simple twist as I like the way it looks. Clean the blade. Do yourself a favor and get Ferric Chloride/PCB Archer Etchant from Radio Shack/online. Each time acid is added, it will eat away at the travertine. Using muriatic acid is no joke, and many DIYers believe it to be a . If you are having trouble getting Ferric, try using Muriatic. Some manufacturers like to roll and cut the pieces into the WD-40 to get the darkest difference. Does muriatic acid etch metal? Apply it to a small area of wet concrete. This is how I do it and it works for me. Once your Damascus is sanded to the correct grit, thoroughly wash it with alcohol and pat dry with a clean rag. Ferric Acid will result in a double grey pattern (dark and light grey pattern) on either a matte or polished finish. Water down with 4 parts water to 1 part ferric. To clean and etch concrete, mix one part muriatic acid to 10 parts water. Hydrochloric acid has a normal pH of 1.5 to 3.5, while muriatic acid has a pH of about 1 to 2. Two popular acids to use are Muriatic acid or feric chloride. This advanced formula incorporates a custom blend of surfactants, organic minerals and derivatives of a plant based extract for the most effective concrete etching solution available. Muriatic acid needs no dilution. Could have probably pypassed this step: dumped 1/2 gallon of phosphoric in the tank and sloshed it around with the cap shut and stoppers in. It's known as muriatic acid and is sold in bulk at pool-supply and home-improvement stores. rideable.org is a participant in the Amazon Services LLC Associates Program, an affiliate advertising program designed to provide a means for sites to earn advertising fees by advertising and linking to amazon.com. Etching is done by exposing the cleaned and polished specimen surface to suitable etching solution such as those described in Table 1. Wash your piece with alcohol and pat it dry with a clean rag. ethanknott, I played with the hot vinegar, didnt like it. on Step 8. Step 1: Sanding Bring your Damascus to a 400 to 600 grit finish. Complete etches in a well ventilated space and wear gloves, eye protection, and an apron or old clothes. I've heard lots of different solution strengths, but 3 parts distilled water to 1 part fecl has worked well for me. The impurities give muriatic acid a yellowish . I love watching Ilya's work. Etching Damascus is a fairly straight forward process that can enhance the appearance of a Damascus blade. Etching. Sign up for a new account in our community. Start very dilute, like 1:10 or 1:20. I agree on the hammer ski Hello Jesse, You don't need a lot. Pour the solution into your watering can you will reduce any splashing using the sprinkle nozzle and the solution will be spread evenly. Toss the PCB into the solution and itll take off. Hang your Damascus piece in the warm acid so that it hangs freely and doesnt touch the sides or bottom of the container. The one thing you DO NOT want when etching Damascus is "fast"..that always equals a poor etch. If you are using ferric acid, lift it with a compact juice until you are so close to 50/50 acid ratio for water supply. Weapons made from Damascus steel are vastly superior to weapons formed from iron! Go MINIMUM of 3-1 dilution with DISTILLED water only. There you are, done! The strength of the acid generally determines how quickly the steel will be etched, the stronger the acid, the faster the process. Beyond that it's a matter of experimentation. Radio Shack sells it online as PCB Etchant. The higher the dilution of the ferric, the slower it will etch, and the better/clean the etch will come out within reason. 90% lower fumes than standard Muriatic Acid. Step 1: What You Need Some damascus steel Etchant - Ferric Chloride (strength 42 baume) Distilled water Acetone Glass or plastic containers Extra fine (000) steel wool Wire (to hang piece in acid) Bucket of water Rubber gloves Baking soda oil (I used olive oil as the knife will be used on food) Ask Question Comment Step 2: Clean It is in a greatly reduced concentration compared to the 30% hydrochloric acid (muriatic acid). Blotchiness in an etch is usually the result of oil somewhere in the system, either on the blade or in the etchant. However by simply etching the look will not be correct for gun barrels, and will be a relatively light contrast. I dont own any Damascus and this is my first, so is that normal? No idea if I'm doing something wrong or if its just part of using vinegar ir if I'm just bad at putting metal into liquids. If you need to warm your acids to be used, the best way to place your acids container is in a large amount of warm water. So I'm lightin' out for the territory, ahead of the scared and the weak and the mean spirited, because Aunt Sally is fixin to adopt me and civilize me, and I can't stand it. Remove the Damascus from the acid and dip it in a bath of baking soda and distilled water to neutralize the acid. Step Three: Applying the Acid Solution. Then I remembered I'd been thinking of switching to re-usable etchant, created on the bench using muriatic acid (the store name for hydrochloric acid, HCl, used for cleaning swimming pools). It is a corrosive salt. For most projects and uses, though, its plenty strong and durable. I plan to buy some ferric chloride pretty soon, or go all mad scientist and make some, but I'd like to get a bit of use out of this $1 vinegar lol. Over the years, Damascus1 has produced various products using one of the four hairdressers of the nazel hair. Ferric Chloride is an iron "salt" of HCl that is nonetheless very acidic, though not as "strong" as HCl. I don't think I'd ever do this, but, dang, I found the whole instructable fascinating. It's expensive, but amazing. Either will etch any high carbon steel, eventually. You will also need to wash a baking bar. As a major metal product on the market, strong power in Damascus is directly related to its quality. I was wondering about the thoughts of cold or rust blui Requests: Array Forseti Steel is a fairly new company that imports what appear to be high quality, handmade knives from Pakistan. Damascus Etching. It is in a greatly reduced concentration compared to the 30% hydrochloric acid (muriatic acid). I etch pretty deeply (3-4 soaks at 15-20 minutes, scrubbing oxides off between soaks) then a light buffing with pink scratchless rouge to bring out the contrast. How do I heat-treat 440C/CPM-154 Damascus billet? When you have mixed the acid solution you can start acid etching the concrete. Mix your Ferric Chloride 1 part to 3 parts of distilled water and put in suitable container. Fill in the etches in good. Copper can be etched with ferric chloride mixed in water to form weak hydrochloric acid. Muriatic acid acts like liquid sandpaper by roughening the surface of the concrete. Radio Shack sells it online as PCB Etchant. If you use muriatic acid, you can bring Damascus up to 1200 grit, or you can leave it 400 grit. As soon as you're done, oil it. Put the holes on both sides or you'll get a bar with raindrop on one side and random on the other. 157K subscribers in the chefknives community. 03-25-2007, 09:56 PM. Chaotic Neutral: Give me liberty, or receive death. Klean-Strip Muriatic Acid can be used to etch concrete, brighten concrete and masonry, or remove excess mortar from bricks. Coffee Etching Damascus Steel | Knife Making How To/Tip Coffee Etching Damascus Steel | Knife Making How To/Tip Watch on The articles on this site are for informational purposes only. thank will wait till summer then to try it. STEP 1: STARTING Bring your Damascus at the end of grit 400 to 600. Damascus Steel the two give much different results. For ferric acid, keep the grit between 400 and 600. Apparently this neutralises the piece as well as helping to set the oxides. 8. If you are having trouble getting Ferric, try using Muriatic. Read entire label prior to use or storage. There are lots of ways and if they work they are correct. In our last etching video, linked below, we ended up using ferric chloride and then sulfuric acid, which didn't give the best results. This comes pre-diluted, but I am not sure what the dilution rate is. The only bad experience is the one from which you learn nothing. etching is completed with chloride with ferric or muriatic acid. Muriatic acid is a powerful and corrosive acidic liquid made from hydrochloric acid, water, and other trace minerals. Everyone has a slightly different dilution and technique. Muriatic also contains some other stuff, typically iron, which is already starting to become ferric. Using an old dental rubber, dial Drums into acids to help remove any fat or fats that may not be available during cleaning, and remove removal materials as acids do their work. Michael, it's easier to add more acid and try again than make it too strong and over-etch. High quality Damascus steel is not the strongest metal you can get. Follow In fact, it is not. You can get an even etch if it's random. Using a broom, scrub the concrete with the acid solution. Earn the Windex deep deep hole so that you can fully fill your Dutch item. How To Acid Etch Metal With Vinegar The Art Of Weapons. . I should mention that this should be done outside since the vapors are stinky and it produces hydrogen gas. I've been there before.. were can you get ferric cloride i've seen diluted in some placesbut havent found full strength, if i see it online they say they cannot ship it. It is a straightforward process, which is used to enhance the appearance of the blade and bring the inherent pattern, lying in wait within the steel, to life. After heat treating, bring your Damascus to a 400 to 600 grit finish. Mix baking soda with distilled water, using a lot of cooking soda so you can dip your piece to reduce acids and stop acne action. Muriatic Acid vs. Hydrochloric Acid How do I heat-treat 3V/CPM-154 Damascus billet? It's used to etch printed circuit boards. [woocommerce-login-nonce] => Before you begin, check the expiration date on your acid of choice to be sure that its not too old. Before you begin, check the expiration date on your acid of choice to be sure that it's not too old. Make sure your steel is clean. Take a high-layer bar and press it between dies that have been drilled full of almost-touching holes, then grind the resulting bumps off. Tweet. Never put acid on the microwave! Nitric Acid - mixture of 5 - 10% nitric acid with the balance being alcohol. Mix the muriatic acid with water (1:10 ratio) in a bucket with the water before the acid, as the other way around will damage the bucket. Etchant - Ferric Chloride (strength 42 baume), oil (I used olive oil as the knife will be used on food). This small board took only 2 minutes. Either is effective. Warm acid gives a much faster etch, but then you get less time to control what's happening. Lol. A standard strength for a careful etch on copper is 42 baume, above this and the ferric will etch more slowly as the solution is viscous. Generally speaking, you want to be at about a 400 grit finish or better to get an even etch across the pattern. has no defect, one of the components inside the steel is not affected by etching, which makes it unacceptable Damascus to be a unique discovery when it's over. ", Damascus's sleeves, guns, and other metallic pieces become more popular as artists and regain their art. Pour the mixture into a plastic garden watering can. The concentration from such sources is typically ~8.9M, or 32% (by mass). If you add additional HCl, the etching solution eventually (after many PCB's) becomes mostly cupric chloride, which is also an excellent etchant. Wanted to compare it with the home-recipe batch I made. It fumes a lot (toxic) and the fumes will rust everything in your shop. Your email address will not be published.

30 Day Extended Weather Forecast Chicago, Wheeling, Wv Drug Arrests, Maureen Straub Below Deck, Articles E